In this manuscript, the electromagnetic wave absorption properties of sustainable porous carbon composites were evaluated over the X-band frequency range (8.2 - 12.4 GHz). The porous carbon material was made from the byproduct of cellulose production and was used as additive on the development of radar absorbing material (RAM) composites. These porous carbon materials have different characteristics, such as porosity size (180 µm < Ø1 < 250 µm and 425 µm < Ø2 < 500 µm) and particle size (ϕ1 < 250 µm and 250 µm < ϕ2 < 425 µm). Composite materials were also studied as frequency selective surface (FSS) structures. It was shown how complex permittivity and reflection loss (RL) can be manipulated over the frequency range using FSS structure. While regular RAM presented RL of 19 dB at ~11.8 GHz, FSS structure presented a RL of 19 dB shifted to 12.4 GHz regarding the same carbon porous material (with particles between 250 and 425 µm and porosity between 180 and 250 µm). It was demonstrated here the potential use of sustainable porous carbon as RAM, and how FSS structure can be used to tune the frequency of the RL maximum peak.

The main challenge for the development of a high efficiency supercapacitor is the electrode material. Developing electrode materials with high specific electrical capacitance and low electrical resistance enables an increase in the energy accumulated in the device. In addition, it is expected that the electrode material presents a simple procedure for preparation having low production cost and being environmentally friendly. This work is based on the deposition of silver nanoparticles on activated carbon felt (Ag@ACF) as a supercapacitor electrode. The samples were characterized by field emission gun scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and textural analysis. Supercapacitor behavior was evaluated by galvanostatic charge-discharge curves, cyclic voltammetry and electrochemical impedance spectroscopy using a symmetrical two-electrode Swagelok type cell, and three different aqueous solution electrolytes: 2 M H2SO4, 6 M KOH and 1 M Na2SO4. Ag@ACF presented a high specific capacitance in KOH, about 170 F g-1, which makes it an interesting material for supercapacitor electrodes and it showed good specific electrical capacitance, low resistance and high cyclability.